高沖級聚苯乙烯
簡介
HI-425是將苯乙烯單體和PBR共聚而成的功能性樹脂, 具有優秀的耐食擊性和耐熱性等, 且特性均衡。
物理特性
| 拉伸強度 (Kg/cm2 at 23°C) | 260 | ASTM D638 |
| 拉伸伸長率 (%) | 50 | ASTM D638 |
| 彎曲強度 (Kg/cm2 at 23°C) | 300 | ASTM D790 |
| 彎曲模量 (Kg/cm2 at 23°C) | 17000 | ASTM D790 |
| Izod 衝擊強度, 6.4mm Notched (Kg.cm/cm) | 9.0 | ASTM D256 |
| 洛氏硬度, L scale | 60 | ASTM D785 |
| 加熱變形溫度 (°C at 6.4mm, 18.8Kg/ cm2 Unannealed) | 74 | ASTM D648 |
| 熔體流動指數 (g/10min at 200°C 5Kg) | 9.0 | ASTM D1238 |
| 成型收縮率 (%) | 0.3-0.6 | ASTM D755 |
| 比重 | 1.04 | ASTM D792 |
| 可燃性 (UL94,HB) | HB | ASTM UL94 |
| 吸水率 (%) | 0.05 | ASTM D570 |
| 絕緣強度 (v/mil) | 450 | ASTM D149 |
| 體積電阻率 (Ω-cm) | 1015 | ASTM D257 |
應用
HI-425用於生產辦公用品、家電産品、各種廚房用具、 日用百貨、玩具、休閑用品等